Канат стальной veropro 8 RS
Product information
Конструкция троса: Veropro 8 RS-це трос из 8 ниток з пластиковим слоем между стальным сердечником и утолщенными внешними переплетениями. Канат в обплетке обеспечивает увеличенную площадь поверхности.
Свойства:
- Очень высокая прочность на разрыв.
- Очень стабильная конструкция каната с очень хорошими усталостными свойствами.
- Пластиковый слой между внутренним и внешним переплетением предотвращает внутренний износ и защищает ядро от коррозии.
ISO 4309
Категория каната : для 42 мм RCN.09, 43-48 мм РКН.11 > 48 мм RCN.13.
- Marking: According to standard
- Standard: EN 12385-4
- Warning: Veropro 8 RS не может использоваться с вертлюгом
- Fill factor: 0.685
- RCN: 09
- Tolerance Ø: +2% to +4%
-
Mobile port crane
-
Offshore crane
-
Crawler crane
Product FAQ
What surface finish and tensile strength does this steel wire rope have?
This steel wire rope has a Galvanized, Bright and is manufactured with a tensile strength of 1960, 2160 N/mm².A bright (uncoated) finish has no corrosion protection and is therefore primarily used in dry, indoor, or controlled environments. Bright wire ropes are generally selected for cost reasons. The galvanized coating provides corrosion protection through a zinc layer, making the rope suitable for outdoor use and humid operating conditions.
Does this steel wire rope have any special design or performance features?
This steel wire rope is compacted, resulting in a smoother surface, higher breaking load, and improved wear resistance compared to standard wire rope constructions. This steel wire rope features internal plastic filling, which improves lubrication retention, reduces internal wire friction, and enhances service life under dynamic loading conditions. This steel wire rope is rotary swaged or hammered, resulting in a compact structure with increased strength, reduced diameter variation, and improved wear resistance.
What is the construction, core type, and lay of this steel wire rope?
This steel wire rope is constructed with 8 strands.
It is manufactured with a steel core, offering higher structural stability, improved resistance to crushing, and reliable performance under heavy loads and multi-layer winding conditions.
It is manufactured with an ordinary right-hand lay (sZ), providing a balanced combination of flexibility, wear resistance, and stable handling. This is the most commonly used lay for general It is manufactured with an ordinary left-hand lay (zS), offering similar performance characteristics to right-hand ordinary lay but designed for specific directional or equipment requirement It is manufactured with a right-hand lang lay (zZ), offering increased abrasion resistance and extended service life in applications where surface wear is a critical factor. It is manufactured with a left-hand lang lay (sS), providing enhanced wear resistance and longer service life where high surface durability is required.